Raise3D Premuim PLA Red
Цена: 2271 ден. (*VAT not icluded.)

Raise 3D PLA or Polylactic acid is a bio-degradable industrial thermoplastic, which is easy to print, durable and relatively strong.

It is also non-toxic and free of unpleasant odor. Parts printed with PLA are widely used in the prototyping stage of product development to prove a concept, check the shape, confirm fit, etc. Models and parts printed with PLA are widely used in product demonstration and presentation in architecture, gaming and movie industries.

 

Check Raise3D printers here

QTY
Description

Raise3D Premium PLA is a premium PLA designed for all desktop FDM/FFF printers.

It ensures consistent extrusion and prevents nozzle jams.

Physical Properties

Typical Value
Density (g/cm3 at 21.5 °C) ASTM D792 (ISO 1183, GB/T 1033)
1.2
Melt index (g/10 min) 210 °C, 2.16 kg
7.0 – 11.0
Glass transition temperature (°C) DSC, 10 °C /min
61
Crystallization temperature (°C) DSC, 10 °C/min
114
The softening temperature of filament (°C) Custom method
129 – 132
Melting temperature (°C) DSC, 10 °C/min
150

Note:
1. Tested with 3D printed specimen of 100% infill.

Mechanical Properties

Property Testing Method
Typical Value Young’s modulus (MPa) (X – Y) ASTM D638 (ISO
527, GB/T 1040) 2636 ± 330

Tensile strength (MPa) (X – Y)
ASTM D638 (ISO 527, GB/T 1040) 46.6 ± 0.9

Elongation at break (%) (X –
Y) ASTM D638 (ISO 527, GB/T 1040) 1.90 ± 0.2

Bending modulus (MPa) (X – Y) ASTM D790 (ISO 178, GB/T 9341)
3283 ± 132

Bending strength (MPa) (X – Y) ASTM D790 (ISO 178,
GB/T 9341) 85.1 ± 2.9

Charpy Impact strength (KJ/m2) (X – Y) ASTM D256 (ISO 179, GB/T 1043)
2.7 ± 0.2